Multilayer Ceramic Capacitors(High Capacitance)
Item
Resistance
to Soldering
Heat
Specification
Appearance : No mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±7.5 %
F, Y5V : within ±20 %
tanδ : Initial standard value
IR : Initial standard value
Withstand voltage : No dielectric breakdown or damage
Test Method
Soldering bath method
Preconditioning : Heat treatment
(½1)
Solder temperature : 270±5 °C
Dipping period : 3.0±0.5 s
Preheat condition :
Order Temp. (°C) Size 0805 max. Size 1206
80 to 100 120 to 180s 300 to 360s
1
2
150 to 200 120 to 180s 300 to 360s
Recovery (Standard condition) : 48±4 h
Soldering bath method
Solder temperature : 230±5 °C
Dipping period : 4±1 s
Solder : H63A (JIS–Z–3282)
Solderability
More than 95 % of the soldered area of both terminal
electrodes shall be covered with fresh solder.
Temperature
Cycle
Appearance : No mechanical damage
Preconditioning : Heat treatment
(½1)
Step 1: Minimum operating temp. 30±3 min
Capacitance change :
Step 2: Room temp. 3 min max.
Temp. Char. B, X7R, X5R : within ±7.5 %
Step 3: Maximum operating temp. 30±3 min
F, Y5V : within ±20 %
Step 4: Room temp. 3 min max.
tanδ : Initial standard value
Number of cycles : 5 cycles
IR : Initial standard value
Recovery(Standard condition) : 48±4 h
Withstand voltage : No dielectric breakdown and/or damage
Preconditioning : Heat treatment
(½1)
Temperature : 40±2 °C
Relative humidity : 90 to 95 %
Test period : 500+24/0 h
Recovery(Standard condition) : 48±4 h
Damp Heat
Appearance : No mechanical damage
(steady state) Capacitance change :
Temp. Char. B, X7R, X5R : within ±20 %
F, Y5V : within ±30 %
tanδ : Temp. Char. B, X7R, X5R : 0.25 max.
F, Y5V : 0.3 max.
IR : 50/C (M ) min.
Note : 10/C (M ) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Please see the technical specifications for details.
Damp Heat
Load
Appearance : No mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±20 %
F, Y5V : within ±30 %
tanδ : Temp. Char. B, X7R, X5R : 0.25 max.
F, Y5V : 0.3 max.
IR : 25/C (M ) min.
Note : 5/C (M ) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Please see the technical specifications for details.
Appearance : no mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±20 %
F, Y5V : within ±30 %
tanδ : Temp. Char. B, X7R, X5R : 0.25 max.
F, Y5V : 0.3 max.
IR : 50/C (M ) min.
Note : 10/C (M ) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Please see the technical specifications for details.
Preconditioning : Voltage treatment
(½2)
Temperature : 40±2 °C
Relative humidity : 90 to 95 %
Applied voltage : Rated voltage
Charge/discharge current : 50 mA max.
Test period : 500+24/0 h
Recovery(Standard condition) : 48±4 h
High
Temperature
Load
Preconditioning : Voltage treatment
(½2)
Temperature : Maximum operation temp. ±3 °C
Applied voltage : (1)Rated voltage 200 %
(2)Rated voltage 150 %
(3)Rated voltage 100 %
Please see the technical specifications
for details.
Charge/discharge current : 50 mA max.
Test period : 1000+48/0 h
Recovery (Standard condition) : 48±4 h
(½1) Heat treatment : 1 h of heat treatment at 150+0/–10 °C followed by 48±4 h recovery under standard conditions.
(½2) Voltage treatment : 1 h of voltage treatment under the specified temperature and voltage for testing followed by 48±4 h of recovery under
standard conditions.
Design and specifications are each subject to change without notice. Ask factory for the current technical specifications before purchase and/or use.
Should a safety concern arise regarding this product, please be sure to contact us immediately.
02 Dec. 2008
– EC5 –
PANASONICBATTERY [ Panasonic Battery Group ]