General Purpose & High Cap.
X7R
6.3 V to 50 V
Surface-Mount Ceramic Multilayer Capacitors
TEST
TEST METHOD PROCEDURE
REQUIREMENTS
IEC 60384- 4.10
21/22
Preheated to a temperature of 80 °C to 140 °C and The solder should cover over 95% of the
Solderability
maintained for 30 seconds to 60 seconds.
critical area of each termination
Test conditions for lead containing solder alloy
Temperature: 235 ±5 °C
Dipping time: 2 ±0.2 seconds
Depth of immersion: 10 mm
Alloy Composition: 60/40 Sn/Pb
Number of immersions: 1
Test conditions for lead-free containing solder alloy
Temperature: 245 ±5 °C
Dipping time: 3 ±0.3 seconds
Depth of immersion: 10 mm
Alloy Composition: SAC305
Number of immersions: 1
4.11
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
No visual damage
Rapid Change of
Temperature
<General Purpose series>
∆C/C
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Class2:
X7R: ±15%
<High Capacitance series>
∆C/C
Recovery time 24 ±2 hours
Class2:
X7R: ±15%
D.F. meet initial specified value
R
ins meet initial specified value