Microwave MLC’s
SQ A Case & B Case Ultra Low ESR MLC
ELECTRICAL SPECIFICATIONS
M&A
Temperature Coefficient (TCC)
(M) +90 ± 20 PPM/ºC ( -55ºC to +125ºC)
(M) +90 ± 30 PPM/ºC ( +125ºC to +175ºC)*
(A)
0 ± 30 PPM/ºC
(M) 0.1 pF to 1000 pF
(A) 0.1 pF to 5100 pF
0.1 pF to 330 pF: from -55ºC to +175ºC*
360 pF to 5100 pF: from -55ºC to +125ºC
Greater than 10,000 at 1 MHz
Greater than 10,000 at 1 MHz
Greater than 2,000 at 1 MHz
Greater than 2,000 at 1 KHz
Greater than 10,000 at 1 MHz
Greater than 2,000 at 1 MHz
0.2 pF to 470 pF
10
6
Megohms min. @ 25ºC at rated WVDC
10
5
Megohms min. @ 125ºC at rated WVDC
510 pF to 5100 pF
10
5
Megohms min. @ 25ºC at rated WVDC
10
4
Megohms min. @ 125ºC at rated WVDC
See Capacitance Values table
250% of rated WVDC for 5 secs
(for 500V rated 150% of rated voltage)
None
None
± (0.02% or 0.02 pF), whichever is greater
C
±15% (-55ºC to 125ºC)
Capacitance Range
Operating Temperature
Quality Factor (Q) M Dielectric A & B Case
A Dielectric B Case
0.001µF to 0.1µF
-55°C to +125°C
2.5% @ 1kHz
0.1 - 200 pF
220 - 1000 pF
1100 - 5100 pF
0.1 - 100 pF
110 - 1000 pF
10
4
Megohms min. @ 25ºC at rated WVDC
10
3
Megohms min. @ 125ºC at rated WVDC
A Dielectric A Case
Insulation Resistance (IR)
Working Voltage (WVDC)
Dielectric Withstanding Voltage (DWV)
Aging Effects
Piezoelectric Effects
Capacitance Drift
* 175 SQCB & SQLB only
See Capacitance Values table
250% of rated WVDC for 5 secs
<3% per decade hour
None
Not Applicable
ENVIRONMENTAL CHARACTERISTICS
AVX SQ will meet and exceed the requirements of EIA-198, MIL-PRF-55681 and MIL-PRF-123
Themal Shock
Moisture Resistance
Low Voltage Humidity
Mil-STD-202, Method 107, Condition A
Mil-STD-202, Method 106
Mil-STD-202, Method 103, condition A, with 1.5 VDC
applied while subjected to an environment of 85ºC with
85% relative humidity for 240 hours
Mil-STD-202, Method 108, for 2000 hours at 125ºC
Mil-STD-202, Method 213, Condition J
Mil-STD-202, Method 204, Condition B
Mil-STD-202, Method 104, Condition B
Mil-STD-202, Method 101, Condition B
Mil-STD-202, Method 208
Mil-STD-202, Method 211
Mil-STD-202, Method 102, Condition C
Mil-STD-202, Method 105, Condition B
Mil-STD-202, Method 210, Condition C
8
Life Test
Shock
Vibration
Immersion
Salt Spray
Solderability
Terminal Strength
Temperature Cycling
Barometric Pressure
Resistance to Solder Heat
120
AVX [ AVX CORPORATION ]