Nichia STSE-CC6112A
<Cat.No.061006>
6.RELIABILITY
(1) TEST ITEMS AND RESULTS
Test Item
Resistance to
Soldering Heat
(Reflow Soldering)
Solderability
(Reflow Soldering)
Thermal Shock
Standard
Test Method
JEITA ED-4701
300 301
JEITA ED-4701
300 303
JEITA ED-4701
300 307
JEITA ED-4701
100 105
JEITA ED-4701
200 203
JEITA ED-4701
200 201
JEITA ED-4701
100 103
JEITA ED-4701
200 202
Test Conditions
Tsld=260°C, 10sec.
(Pre treatment 30°C,70%,168hrs.)
Tsld=215 ± 5°C, 3sec.
(using flux, Lead Solder)
-40°C ~ 110°C
1min. (10sec.) 1min.
(Pre treatment 30°C,70%,168hrs.)
-40°C ~ 25°C ~ 110°C ~ 25°C
30min. 5min. 30min. 5min.
25°C ~ 65°C ~ -10°C
90%RH 24hrs./1cycle
Ta=110°C
Ta=60°C, RH=90%
Ta=-40°C
Ta=25°C, I
F
=30mA
Ta=85°C, I
F
=25mA
60°C, RH=90%, I
F
=20mA
Ta=-40°C, I
F
=20mA
JEITA ED-4701
500 501
JEITA ED-4701
400 403
Solvent : Isopropyl Alcohol
Solvent Temperature : 20 ~ 25°C
Dipping Time : 5 min.
100 ~ 2000 ~ 100Hz Sweep 4min.
200m/s
2
3direction, 4cycles
75cm
R=1.5kΩ, C=100pF
Test Voltage=2kV
Note
2 times
Number of
Damaged
0/22
1 time
over 95%
100 cycles
0/22
0/100
Temperature Cycle
Moisture Resistance Cyclic
High Temperature Storage
Temperature Humidity
Storage
Low Temperature Storage
Steady State Operating Life
Steady State Operating Life
of High Temperature
Steady State Operating Life
of High Humidity Heat
Steady State Operating Life
of Low Temperature
Permanence of Marking
100 cycles
10 cycles
1000 hrs.
1000 hrs.
1000 hrs.
1000 hrs.
1000 hrs.
1000 hrs.
1000 hrs.
1 time
0/100
0/100
0/100
0/100
0/100
0/100
0/100
0/100
0/100
0/22
Vibration
48min.
0/10
Drop
Electrostatic Discharge
JEITA ED-4701
300 304
3 times
3 times
Negative/Positive
0/10
0/22
(2) CRITERIA FOR JUDGING DAMAGE
Item
Forward Voltage
Luminous Intensity
Condition 1
Luminous Intensity
Condition 2
Symbol
V
F
I
V
I
V
Test Conditions
I
F
=20mA
I
F
=20mA
I
F
=20mA
Criteria for Judgement
Min.
Max.
-
L.S.L.**)
L.S.L.**)
0.7
0.5
U.S.L.*)
-
-
1.1
*) U.S.L. : Upper Standard Level
**) L.S.L. : Lower Standard Level
These test items are judged by the criteria of Luminous Intensity Condition 2.
-3-
NICHIA [ NICHIA CORPORATION ]